以磷酸二氢铵(MAP)溶液为阻燃剂,通过浸泡尾叶桉单板,研究了单板的载药量;以Ⅱ类胶合强度为指标,利用正交试验对常规胶合板生产工艺进行了优选。在此基础上,选取浸泡时间和最优生产工艺试制了阻燃桉树胶合板,并对其Ⅱ类胶合强度和燃烧性能进行了检测。结果表明:不同厚度尾叶桉单板的载药量随浸泡时间的延长呈现相似的增长规律;试验所得常规尾叶桉胶合板最优生产工艺为施胶量210 g.m-2、热压温度130℃、热压时间8 min,该条件下胶合板的Ⅱ类胶合强度达到了2.01 MPa;单板浸泡8h后,单板平均载药量为32.05 kg.m-3,所制得阻燃胶合板氧指数提高了13.9%,炭化长度减少了8.3 mm(26.2%),阻燃性能明显提高,而胶合强度也达到了Ⅱ类胶合板的国家标准。研究初步证明利用常规桉树胶合板生产工艺生产阻燃桉树胶合板是可行的。

Based on the results of more than ten year's scientific research and practice, some key techniques for cultivating poplar veneer glued wood were summarized systematically. The results were as follows: (1)Selecting appropriate poplar clones for various cultivation zones according to their growth rate and wood quality. (2)Choosing good sites being suitable for poplar clone growing (at least SI≥18?m). (3)Adopting reasonable planting density which can produce more timbers to meet the need of plywood(the tree spacing should be more than 5?m×5?m). (4)Using correct planting methods for different soil conditions, however, large seedling with 2 year old root and 1 year old stem (seedling height>4?m)were advocated. (5)Taking effective measures to tend the stand, the most effective measure was interplanting with crops. (6)Pruning was neccessary to produce non node timber, but pruning method, pruning intensity and pruning season should be controlled properly. If the 6 measures mentioned above were carried out, the poplar forests with a high yield and high quality could be ensured. In order to provied some theoretical basis for cultivating poplar veneer glued wood, 4 optimum cultivation patterns were also established using the method of two dimensions system.